product description
K2 HF - High Fusing
K2 HF is a high-fusing metal ceramic with excellent optical and physical properties. It is fired at 910°C and is suitable for almost all alloys with a CTE of 13.8 - 14.9 / 25° - 500°C. If the CTE is higher than 14.5, long-term cooling is recommended.
Shades overview
Firing parameters K2 HF |
|||||||
starting temperature | dry | increase temperature | vacuum | final temperature | hold time | result | |
Oxid brand | Depending on the alloy manufacturer‘s instructions | ||||||
Bonder brand | Recommended for non precious metal! When using bonder only 1 opaque firing is necessary! | shiny | |||||
550°C / 1022°F | 6 min | 80°C (176°F) / min | + | 980°C / 1796°F | 1 min | ||
1. Opaque firing powder* |
590°C / 1094°F | 4 min | 75°C (167°F) / min | + | 950°C / 1742°F | 1 min | shiny |
2. Opaque firing powder |
590°C / 1094°F | 4 min | 75°C (167°F) / min | + | 940°C / 1724°F | 1 min | slightly shiny |
Shoulder firings | 550°C / 1022°F | 4 min | 80°C (176°F) / min | + | 930°C / 1706°F | 1 min | slightly shiny |
Dentin firing | 570°C / 1058°F | 6 min | 50°C (122°F) / min | + | 910°C / 1670°F | 1 min | slightly shiny |
Correction firing | 570°C / 1058°F | 5 min | 50°C (122°F) / min | + | 900°C / 1652°F | 1 min | slightly shiny |
Glaze firing | 590°C / 1094°F | 3 min | 50°C (122°F) / min | - | 895°C / 1643°F | 1 min | shiny |
Glaze firing with glaze | 500°C / 932°F | 3 min | 45°C (113°F) / min | - | 855°C / 1571°F | 1 min | shiny |
* For non precious alloys final temperature 960°C Firing Parameters are Guidelines and need to be adjusted to the situation of the furnace! The right firing result is important! |
|||||||
Changes and errors excepted! |